There is a saying:&quo; It doesn't matter who you are, what matters is who you are with& Rdquo; Card friends will urge you to play cards, wine friends will toast you, but positive energy friends will make you become positive and upward. Just like when we make metallographic samples, we choose metallographic consumables. What kind of metallographic consumables you choose will present what kind of samples,


So, who we are with is really important; Choosing the right consumables for metallographic sampling is also really important. Let's take a look at the consumables for metallographic sampling that our engineers have a high usage rate, following the editor of Chain Energy!


There are many brands and types of metallographic sample making consumables, but engineers mainly prefer and commonly use the following three types of American QMAXIS metallographic consumables:

          Metallographic sample making consumables: 1. The original imported QMAXIS (Kemai) ultra-thin grinding wheel cutting blades are suitable for metallographic precision cutting machines and metallographic grinding wheel cutting machines, respectively. The thickness of ultra-thin grinding wheel cutting pieces is slightly thicker than diamond&CBN cutting pieces and slightly thinner than grinding wheel cutting pieces. This ultra-thin grinding wheel cutting blade has small incisions, minimal damage, high cutting efficiency, wide application range, and long service life. In many application scenarios, replacing diamond&CBN cutting blades is an effective choice for metallographic sample preparation engineers to reduce costs and increase efficiency.


&Flash& Flash; Ultra thin grinding wheel cutting blades with an axial aperture of 12.7mm: 4in, 5in, 6in, 7in, 8in


&Flash& Flash; Ultra thin grinding wheel cutting blades with an axial aperture of 32mm: 10in, 12in

          Metallographic sample preparation consumables 2. Original imported QMAXIS (Kemai) cold embedding resin and curing agent from the United States, including epoxy resin system and acrylic resin system. Low viscosity, low shrinkage rate, strong permeability, and good edge protection effect, suitable for room temperature inlay of materials sensitive to temperature and pressure. The operation is simple, convenient, and widely used, making it very suitable for single batch sample preparation.


&Flash& Flash; EpoQuick epoxy resin and curing agent, 2 hours


&Flash& Flash; EpoCure epoxy resin and curing agent, 6h


&Flash& Flash; EpoFlow epoxy resin and curing agent, 9h


&Flash& Flash; EpoLi ion epoxy resin and curing agent, 24h/25 ℃ or 2h/60 ℃


&Flash& Flash; AcryQuick acrylic resin and curing agent, 8-12 minutes

          Metallographic sample preparation consumables 3. The original imported QMAXIS (Kemai) silicon carbide metallographic sandpaper from the United States has strong toughness, good water resistance, uniform, dense, sharp distribution of silicon carbide particles, and high removal rate. By grinding the metallographic sample with it, the surface scratch is small and the consistency is good, which is conducive to the subsequent polishing process and can effectively shorten the sample preparation time.


&Flash& Flash; CarbiPaper with adhesive backing silicon carbide sandpaper


&Flash& Flash; CarbiPaper without backing adhesive, silicon carbide sandpaper